China hot work tool steel(H11/1.2343/SKD6)
Quenching and Tempering specification: Preheat temperature 790° C, Quenching Temperature 1000° C(Salt bath) or 1010° C(Controlled atmosphere), heat preservation 5~15min, then air cooling; Tempering temperature 550° C, hardness≥ 60HRC.
Gas n... |
2017-12-19 |
 |
Hot Work Tool Steel(1.2343/X38CrMoV5-1)
Chemical Composition C Si Mn | P≤ | S≤ | Cr |
|  |
high shock resistant tool steel
1.2510 100MnCrW4Â is a high quality non-distorting cold work tool steel. 1.2510 100MrCrW4 has combined manganese chromium tungsten and is characterised by giving high surface hardness after heat treatment and tempering, good dimensional stability in... |
2017-12-15 |
 |
cold work tool steel
1. Conditions of delivery
EAF/ESR，forged/hot rolled，black/turned（milled），annealed，HB≤250
According to your need…
2. Size：
Thickness：Produced by your requirements
Width：Produced by your requirements
Diamete... |
2017-12-14 |
 |
Shock Resistant Tool Steel (S-7 Impact Resistant Tool Steel )
S7 is a shock-resistant air hardening tool steel, designed for high impact resistance at relatively high hardness. It offers toughness to withstand chipping and breaking, combined with high attainable hardness and good wear resistance.  C.Si.Mn.Cr.... |
2017-12-03 |
 |
China high speed tool steel(M2/SKH9/1.3343)
... |
2017-12-02 |
|
China high speed tool steel(M2/SKH9/1.3343)
... |
2017-11-30 |
 |
China hot work tool steel(H11/1.2343/SKD6)
Quenching and Tempering specification: Preheat temperature 790° C, Quenching Temperature 1000° C(Salt bath) or 1010° C(Controlled atmosphere), heat preservation 5~15min, then air cooling; Tempering temperature 550° C, hardness≥ 60HRC.
Gas nitridi... |
2017-11-29 |